Optimization of preparation process for walnut shell-based wood particleboard

Abstract

Driven by the “double carbon” strategy, aiming at the potential of walnut shell, an agricultural and forestry waste, to replace wood in particleboard production, this study used walnut shell powder and wood shavings as raw materials, with melamine-modified urea-formaldehyde resin as the adhesive. A four-factor, three-level orthogonal experiment was conducted to investigate the effects of hot-pressing temperature, pressure, duration, and adhesive application level on the physical and mechanical properties of the panels. The optimal process conditions were 160°C, 4 MPA, 6 min, and a 14% adhesive application percentage. Under these conditions, the panel had a density of 0.70 g/cm³, and its modulus of rupture (MOR), modulus of elasticity (MOE), internal bonding strength (IB), and 2-hour thickness swelling (2hTS) all exceeded the limits specified in GB/T 4897 (2015) by 30% to 60%. The order of influence of each parameter was hot-pressing temperature > adhesive application level > hot-pressing pressure > hot-pressing duration. This study established for the first time the optimal process window for walnut shell-based particleboard, demonstrating that a 30% wood substitution can balance performance and resource conservation, providing technical support for the green and high-value utilization of agricultural and forestry wastes.

Full Article

Optimization of Preparation Process for Walnut Shell-based Wood Particleboard

RenFen Liu  ,* JiFei Chen, Guo Xiang, and WenGang Chen

Driven by the “double carbon” strategy, aiming at the potential of walnut shell, an agricultural and forestry waste, to replace wood in particleboard production, this study used walnut shell powder and wood shavings as raw materials, with melamine-modified urea-formaldehyde resin as the adhesive. A four-factor, three-level orthogonal experiment was conducted to investigate the effects of hot-pressing temperature, pressure, duration, and adhesive application level on the physical and mechanical properties of the panels. The optimal process conditions were 160°C, 4 MPA, 6 min, and a 14% adhesive application percentage. Under these conditions, the panel had a density of 0.70 g/cm³, and its modulus of rupture (MOR), modulus of elasticity (MOE), internal bonding strength (IB), and 2-hour thickness swelling (2hTS) all exceeded the limits specified in GB/T 4897 (2015) by 30% to 60%. The order of influence of each parameter was hot-pressing temperature > adhesive application level > hot-pressing pressure > hot-pressing duration. This study established for the first time the optimal process window for walnut shell-based particleboard, demonstrating that a 30% wood substitution can balance performance and resource conservation, providing technical support for the green and high-value utilization of agricultural and forestry wastes.

DOI: 10.15376/biores.21.1.2004-2024

Keywords: Walnut shell; Particleboard; Carbon neutralization; Process parameter optimization; Orthogonal experiments

Contact information: School of Mechanical and Transportation Engineering, Southwest Forestry University, Kunming, Yunnan 650224, China; *Corresponding author: cjf100cjf@163.com

Graphical Abstract

INTRODUCTION

Driven by the “double carbon” strategy, forest resources—as the largest terrestrial carbon sink—are facing unprecedented pressure (Zhang et al. 2022). Although the international community has set the goal of achieving carbon neutrality, the wood-based panel industry currently finds itself in a challenging situation. With the rapid increase in global demand for particleboard, excessive logging has caused timber prices to rise steadily, thereby undermining the foundational role of forests as carbon sinks in the path toward carbon neutrality. More concerning is the fact that millions of tons of walnut shells—by-products of the global nut processing industry—are directly landfilled annually worldwide. Unlike wood shavings that require dedicated forest harvesting, walnut shells represent a zero-cost, renewable waste stream with no additional carbon sink depletion. As lignocellulosic biomass resources, these materials not only emit significant amounts of methane during decomposition, but they also generate leachate, posing a dual threat to groundwater systems (Kjeldsen et al. 2002). Critically, walnut shells differ from conventional wood raw materials in their higher lignin content (28 to 35% vs. 20 to 25% in softwood) and dense cell wall structure (Pirayesh et al. 2012; Kumar et al. 2023). This distinctive composition endows them with superior hardness (Brinell hardness ~25 HB vs. 15 to 20 HB in pine wood) and water resistance. These are key properties for improving particleboard durability, which cannot be achieved by wood shavings alone. Breaking through this dilemma requires the establishment of a new circular economy model. Recent studies have shown that walnut shells, due to their unique microstructure and chemical composition, can serve as an alternative raw material for high-quality wood. Barbu et al. (2020) found that particleboards manufactured with walnut shell exhibit higher dimensional stability and Brinell hardness compared to cork-based particleboards. Pirayesh et al. (2013) and da Silva et al. (2017) reported that using walnut shell in combination with urea-formaldehyde adhesive significantly reduces formaldehyde emissions, with the effect being irreversible in the presence of formaldehyde and dodecane.

Sarsari et al. (2016) investigated the potential application of walnut shell powder (WSF) as a wood substitute in thermoplastic starch (TPS) composites and its influence on material properties. When the WSF content reached 40%, the tensile strength, flexural strength, and elastic modulus of TPS-based composites were significantly enhanced. Furthermore, Ayrilmis et al. (2013) reported that in polypropylene composites, the incorporation of WSF resulted in increased flexural and tensile moduli and improved thermal stability (Dobrzyńska-Mizera et al. 2019). Hamidreza Pirayesh et al. (2012) utilized a mixture of walnut shell and wood particles to fabricate particleboard. The addition of walnut shell particles substantially improved the water resistance of the panels—with water absorption reduced by 15 to 20% compared to pure wood particleboard. This can be attributed to their dense lignin-rich structure that inhibits water penetration (Pirayesh et al. 2012). While the proportion of walnut shells should not exceed 20% to meet the required standard for modulus of rupture (MOR) of pure wood particleboard, this limitation can be addressed by optimizing pressing parameters (a gap this study aims to fill). Notably, even at 20% addition, the thickness swelling of the composite board was reduced by 12% (Pirayesh et al. 2012). Such a performance enhancement cannot be achieved with the use of wood shavings without additional chemical treatments, which increase production costs and environmental impact.

Kumar et al. (2023) found that lignin and cellulose are essential components of lignocellulosic raw materials used for particleboard production, contributing significantly to enhanced mechanical strength and adhesive efficiency. Unlike wood shavings (cellulose 40 to 45%, lignin 20 to 25%), walnut shell powder is characterized by higher lignin content (28 to 35%) and lower hemicellulose content (15 to 18% vs. 25 to 30% in wood) (Pirayesh et al. 2012). This composition not only enhances the material’s hardness and strength—improving particleboard MOR by 8 to 10% when substituted for 15 to 20% of the wood shavings—but it also reduces adhesive demand. The dense lignin structure promotes better interfacial bonding with urea-formaldehyde adhesive, lowering usage by 10 to 12% compared to pure wood formulations (da Silva et al. 2017). Furthermore, as a filling material (Dobrzyńska-Mizera et al. 2019), WSF not only reduces the dependence on wood shavings (alleviating logging pressure on carbon sinks and supporting the “double carbon” strategy proposed by Zhang et al. (2022)) and the amount of adhesive required, but it also enhances physical properties such as lowering water absorption and increasing heat resistance (thermal decomposition temperature increased by 15 to 20 °C). This is a critical advantage for particleboard used in high-temperature environments (e.g., kitchen cabinets). Therefore, using walnut shells as a raw material for particleboard aligns with the growing trend toward sustainable and eco-friendly materials. The alignment is not only due to waste valorization but also for its unique ability to improve product performance while reducing costs and environmental impact—advantages that conventional wood raw materials cannot replicate. However, none of the studies have examined the pressing parameters involved in walnut shell particleboard manufacturing or clarified how factors, such as hot-pressing pressure, time, temperature, and adhesive dosage, affect the final product’s physical properties. Thus, this study aimed to identify the key factors—hot-pressing temperature, pressure, time, and glue dosage—that influence the mechanical performance of walnut shell-based particleboards, providing a direct technical foundation for the environmentally responsible and high-value utilization of agricultural and forestry residues and further supporting the realization of carbon neutrality goals (Zhang et al. 2022).

EXPERIMENTAL

Main Material

Walnut shells were sourced from local walnut growers (Yunnan Province, China, a major walnut-producing region). After crushing, screening, and drying, they were processed into powder (20 to 35 mesh, 10% moisture content). Wood shavings were supplied by Feilin Wood-Based Panel Group Co., Ltd. (Kunming, China). The shavings (a typical commercial particleboard mix) contained ~60 to 65% hardwood (mainly Populus spp., Eucalyptus spp.) and 35 to 40% softwood (primarily Pinus spp.), with 3% moisture content and 30 to 50 mm dimensions. The adhesive was self-prepared melamine-modified urea-formaldehyde resin (64% ± 2% solid content, pH 8.1, viscosity 410 mPa·s).​

Main Instruments and Equipment

The primary experimental instrument employed in this study comprised hygrometers, hot presses, mechanical testing machines, and data analysis software. The experimental instruments are shown in Table 1.

Table 1. Experimental Instruments and Analysis Software

Method

Experiment on the proportion of walnut shell powder

A melamine-modified urea-formaldehyde resin adhesive, exhibiting excellent water resistance, aging resistance, and low formaldehyde emission (Xi et al. 2024), was used to evaluate the performance of walnut shell powder and wood shavings at varying mixing ratios. Under consistent process parameters, particleboards were fabricated, and their mechanical and physical properties—including modulus of rupture (MOR), modulus of elasticity (MOE), internal bonding strength (IB), and 2 h thickness swelling percentage (2hTS)—were systematically tested and analyzed.

Process test of walnut shell-based wood particleboard

An L9 (3⁴) orthogonal array test was conducted, with hot-pressing temperature, hot-pressing pressure, hot-pressing duration, and adhesive application level designated as variable factors. This methodology provides a straightforward, systematic, reliable, and highly effective approach to minimizing experimental error through the identification of optimal parameter settings, thereby reducing the number of required trials, associated costs, and processing time. The process conditions for walnut shell-based wood particleboard were optimized based on key performance indicators including MOR, MOE, IB, and 2hTS. Average values were determined from repeated measurements. Details of the experimental design are presented in Table 2.

Table 2. Factor Levels for the Orthogonal Test

Preparation process of particleboard

The walnut shells were dried to reduce their moisture content to 10%. After drying, the walnut shells were crushed using a universal pulverizer via a stepwise crushing method: first, coarse crushing was performed to reduce the shells to a particle size of 5 to 10 mm, followed by fine crushing to further refine the particles. The crushed material was then sieved to obtain walnut shell powder with an appropriate particle size (20 to 35 mesh), and oversize or undersize particles were discarded to ensure uniform particle size distribution. Based on a target density of 0.7 g/cm³ (plate specification: 300 mm × 350 mm × 10 mm), the quantity of raw materials was calculated, and wood shavings were blended with walnut shell powder at a mass ratio of 3:7. To ensure even adhesive distribution, the adhesive application level was maintained at 8% to 12% of the dry raw material weight. The mixture of raw materials and adhesive was then homogenized through manual stirring. Subsequently, the mixture was formed into a uniformly structured slab; internal air was removed by pre-pressing the compacted slab at a pressure of 0.5 to 1.0 MPa. The hot-pressing stage (core process) was conducted under the following conditions: temperature 160 to 200°C; pressure 3.0 to 5.0 MPa; time 6 to 8 min for plates with a thickness of 10 mm. Through the synergistic effects of temperature, pressure, and time, adhesive curing and plate densification were achieved. To prevent delamination, a gradient pressure release method was applied. After hot pressing, the sheets were cooled to an internal temperature below or equal to 40 °C to stabilize their structure, followed by a seven-day conditioning period in a controlled environment to relieve residual stress. Finally, the treated sheets were cut into standard specimens using a horizontal band saw machine; all cuts were performed at a feed rate of 300 mm/min to ensure flat, burr-free surfaces and avoid structural damage to the specimens, and key performance indicators—including MOR, MOE, IB, and 2hTS—were evaluated. The preparation process of walnut shell-based wood particleboard is illustrated in Fig. 1.

Fig. 1. Preparation process of walnut shell-based wood particleboard

The mechanical properties—including MOR, MOE, IB, and 2hTS—of walnut shell-based wood particleboard were evaluated in accordance with GB/T 17657 (2022).

Modulus of rupture

The MOR is a critical mechanical property that characterizes the bending failure resistance of particleboard. It is defined as the ratio of the bending moment at fracture to the section modulus of the specimen under maximum load, expressed in MPa. According to GB/T 17657 (2022), samples were cut into dimensions of 250 mm (length) × 50 mm (width). The MOR was determined using a universal mechanical testing machine operating on the three-point bending principle and calculated in accordance with Eq. 1,

 (1)

where F_max denotes the maximum load at specimen failure, expressed in Newtons (N); l₁ represents the distance between the two supports, measured in millimeters (mm); b indicates the specimen width (mm); and t² refers to the specimen thickness (mm).

Modulus of elasticity

The MOE serves as a key mechanical performance indicator that reflects the material’s resistance to deformation within the elastic range. It is defined as the ratio of stress to strain produced under load within the material’s elastic limit, expressed in MPa. As specified in GB/T 17657 (2022), specimens were prepared with dimensions of 250 mm (length) × 50 mm (width). The MOE was determined using a universal mechanical testing machine operating on the three-point bending principle and calculated in accordance with Eq. 2,

 (2)

where denotes the distance between two supports, expressed in millimeters (mm); b indicates the specimen width (mm); t³ refers to the specimen thickness (mm); F₂–F₁ represents the load increment within the linear segment of the load-deflection curve, where F₁ corresponds to approximately 10% of the maximum load and F₂ to approximately 40%, all values expressed in Newtons (N). The deformation difference at midpoint a₁–a₂ reflects the deflection change of the specimen under the applied force interval from F₂ to F₁, measured in mm.

Internal bond

The IB is defined as the ratio of maximum tensile force to the load-bearing area between fibers or particles within the plate, resulting from bonding failure when tensile stress is applied perpendicular to the particleboard surface. It is expressed in MPa. As specified in GB/T 17657 (2022), specimens were prepared with dimensions of 50 mm × 50 mm, and IB was determined using a universal mechanical testing machine. The calculation followed Eq. 3,

 (3)

where F_max denotes the maximum load at specimen failure, expressed in Newtons (N); l represents the specimen length in millimeters (mm); and b indicates the specimen width in millimeters (mm).

Two-hour thickness swelling

The thickness swelling is defined as the percentage increase in the thickness of particleboard after being immersed in water for 2 h. The test procedure complies with GB/T 17657 (2022). A standard-sized specimen (typically 50 × 50 mm) is immersed in water maintained at 20 °C for 2 h, and the thickness change before and after water absorption is precisely measured using a micrometer with a resolution of 0.01 mm. The calculation follows Eq. 4,

 (4)

where t₂ denotes the specimen thickness after immersion and t₁ represents the specimen thickness before immersion, both expressed in millimeters (mm).

RESULTS AND DISCUSSION

Test Results

Test results regarding the proportion of walnut shell powder

The effects of different proportions of walnut shell powder on the key physical properties of particleboard are presented in Table 3.

Table 3. Relationship between the Proportion of Walnut Shell Powder and the Physical Properties of Particleboard

Fig. 2. SEM images of walnut shell particleboard with a proportion of 30% and a particle size of 20 to 35 mesh; a: scale bar of 1 mm, b: scale bar of 200 μm

As shown in Table 3, when the proportion of walnut shell powder was 0% (i.e., for pure wood particleboard), the board exhibited relatively high MOR and MOE, both of which far exceeded the standard values. In contrast, its 2hTS was significantly below the standard requirement, indicating poor water resistance stability of the board. When the proportion of walnut shell powder reached 15%, the MOR, MOE, and IB values all significantly exceeded the standard requirements. However, the wood substitution level remains low under this proportion, resulting in limited benefits for resource conservation. When the walnut shell powder content was increased to 30%, the mechanical properties of the particleboard (MOR, MOE, and IB) only met the minimum standard thresholds. As shown in Fig. 2, at a walnut shell proportion of 30% and a particle size of 20 to 35 mesh, the walnut shell particles were tightly bonded not only with each other but also with wood particles. The adhesive effectively filled the voids and coated both types of particles, suggesting that this particle size is suitable for achieving good interfacial adhesion. Hamidreza Pirayesh et al. (2012) investigated a mixture of walnut shell and wood particles for manufacturing particleboard. Their results indicated that the maximum allowable walnut shell content should not exceed 20% to satisfy the modulus of rupture requirements. To meet the mechanical performance criteria while maximizing wood substitution and addressing the limitation of a 20% maximum walnut shell content, a formulation containing 30% walnut shell powder with a particle size of 20 to 35 mesh was selected as the baseline for subsequent optimization experiments.

Results of the orthogonal experiment

In this study, the key factors influencing the mechanical properties of walnut shell-based wood particleboard—namely hot-pressing temperature, hot-pressing pressure, hot-pressing duration, and adhesive application level—were investigated using an orthogonal experimental design. Table 4 presents the experimental design parameters and the corresponding physical and mechanical property test results.

Table 4. Orthogonal Experimental Design and Results

Through comparing the results with GB/T 4897 (2015), it can be confirmed that the MOR, MOE, IB, and 2hTS values of the third group in Table 3 met the required standards. Therefore, it can be preliminarily inferred that the particleboard performance was improved under the following conditions: a hot-pressing temperature of 160 °C, a hot-pressing pressure of 5 MPa, a hot-pressing duration of 8 min, and an adhesive application level of 14%.

Technical Index Analysis

As shown in Fig. 3, the range of hot-pressing temperature for the three groups (MOR, MOE, and IB) is the largest among all four factors, indicating that hot-pressing temperature had the most significant influence on the MOR, MOE, and IB performance of walnut shell-based wood particleboard. Conversely, its impact on 2hTS was minimal. With increasing temperature, both MOR and MOE values decreased significantly, whereas 2hTS rose sharply. The range of adhesive application level across all four test groups was also considerable, particularly for 2hTS, which suggests a strong effect of adhesive application level on overall sheet properties. 

Fig. 3. Range analysis of the orthogonal test: a) MOR range analysis, b) MOE range analysis, c) IB range analysis, and d) 2hTS range analysis; Note: K₁ represents the first mean, K₂ represents the second mean, K₃ represents the third mean, and R represents the range

To efficiently assess the extent of influence exerted by four key factors—hot pressing temperature, pressure, duration, and resin application level—on the physical and mechanical properties of particleboard and to determine whether these factors significantly affect the experimental outcomes, both range analysis and variance analysis were carried out based on the results of the orthogonal test, as illustrated in Fig. 3.

As the adhesive application level increased, MOR, MOE, and IB values demonstrated a clear upward trend, while 2hTS declined correspondingly. Hot-pressing pressure likewise affected all four mechanical properties; as pressure increased, MOR and IB increased, whereas MOE and 2hTS tended to decrease. Among the four factors analyzed, hot-pressing duration exerted the least influence on the mechanical behavior of the particleboard. Overall, the factors were ranked in the order of influence as hot-pressing temperature > adhesive application level > hot-pressing pressure > hot-pressing duration.

Table 5. Variance Analysis of the Orthogonal Test

Table 5 demonstrates that at the α = 0.01 significance level, hot-pressing temperature significantly influenced both MOR and MOE of the board, while the adhesive application level significantly affected 2hTS. At the α = 0.05 level, the glue application amount remained a significant factor for MOR, whereas hot-pressing pressure and duration showed no statistically significant effects on any of the measured indices. The overall influence of hot-pressing temperature exceeded that of adhesive application level. This finding aligns with the range analysis results presented in Fig. 3, which indicate the following order of factor importance: hot-pressing temperature > adhesive application level > hot-pressing pressure > hot-pressing duration. These findings suggest that hot-pressing temperature and adhesive application level should be prioritized during the preparation of walnut shell-based wood particleboard, as they have a substantial impact on its mechanical performance.

The underlying mechanism can be attributed to two key factors: under optimal hot-pressing conditions, a higher adhesive application level enhances the contact area between particles and adhesive. Concurrently, elevated hot-pressing temperatures improve particle plasticity and accelerate adhesive curing, resulting in more complete bonding. Together, these effects contribute to improved structural strength, stability, and inter-particle adhesion. Furthermore, the adhesive layer formed on particle surfaces acts as a barrier to water penetration (Gonçalves et al. 2018), thereby reducing the thickness swelling of the final product.

Effect of Hot-pressing Temperature on Mechanical and Physical Properties of Walnut Shell-Based Wood Particleboard

The hot-pressing temperature is a critical parameter in the hot-pressing process. An appropriate temperature allows the slab interior to rapidly reach the required curing temperature for the adhesive, thereby enhancing both curing efficiency and mechanical properties of the particleboard (Ji and Lei et al. 2023). Under conditions of a hot-pressing pressure of 5 MPa, hot-pressing duration of 8 min, and resin application level of 14%, the effects of varying hot-pressing temperatures on particleboard properties are presented in Fig. 4.

Fig. 4. The influence of hot-pressing temperature on the Mechanical and Physical Properties of walnut shell-based wood particleboard

Note: *** indicates that the effect is extremely significant at p < 0.001,** indicates that the effect is extremely significant at p < 0.01, and * indicates that the effect is significant at p < 0.05.

As shown, the MOR and MOE decreased with increasing hot-pressing temperature. When the temperature was excessively high, volume expansion increased, resulting in greater damage at bonding interfaces under different environmental conditions. The IB strength exhibited a non-monotonic response to hot-pressing temperature. The initial increase can be attributed to enhanced thermoplastic flow of lignocellulosic components and accelerated adhesive curing (Wei et al. 2021; Zhang et al. 2021), followed by a decline due to excessive degradation of wood polymers and premature cross-linking of adhesives (Li et al. 2023). The 2hTS increased with rising hot-pressing temperature. Higher temperatures induce hemicellulose degradation in walnut shell composites, generating hydrophilic oligosaccharides and increasing pore volume. This layered porosity enhanced capillary water absorption. Compared to low-temperature processing, the 2hTS value was significantly higher (Hashim et al. 2011). As illustrated in Fig. 4, there was a notable difference between static bending strength and elastic modulus, indicating that hot-pressing temperature had a significant influence on these mechanical properties. In contrast, the variation in 2hTS was relatively minor, indicating limited sensitivity to temperature changes. This aligns with the range and variance analysis results presented in Fig. 3 and Table 5. Furthermore, examining the significance levels in the figure reveals that at 160 °C, favourable effects were observed for bending properties (higher MOR and MOE) and dimensional stability (lower 2hTS); 180 °C represented the optimum temperature for internal bond strength, with MOR and IB meeting industry standards, though MOE and 2hTS fell short; 200 °C led to diminished mechanical properties and heightened swelling, potentially stemming from excessive adhesive curing or thermal degradation of the lignin-cellulose fraction, thereby compromising interfacial bonding and material stability. Overall, the comprehensive assessment indicated that the optimum hot-pressing temperature for walnut shell-based particleboard was approximately 160 °C.

Effect of Hot-pressing Pressure on the Mechanical and Physical Properties of Walnut Shell-Based Wood Particleboard

Hot pressing is one of the key processes in plate-making, which directly influences the density, MOR, MOE, IB, and other mechanical properties of the particleboard. Under conditions of a hot-pressing temperature of 160 °C, a hot-pressing duration of 8 min, and an adhesive application level of 14%, the effects of varying hot-pressing pressures on board properties are illustrated in Fig. 5.

Fig. 5. Effect of hot-pressing pressure on the mechanical and physical properties of walnut shell-based wood particleboard

Both MOR and IB increased with rising pressure, as higher pressure enhanced adhesive penetration into wood fibers, thereby strengthening interfacial bonding. This mechanism contributes to a proportional increase in MOR and IB values (Kang et al. 2021). In contrast, MOE decreased with increasing pressure. Under high-pressure conditions, the curing rate of adhesives accelerates; however, excessive pressure may hinder steam release, leading to microcracks or delamination between particles, which ultimately reduces the elastic MOE (Kang et al. 2021). The 2hTS initially decreased and then increased with increasing hot-pressing pressure. This trend can be attributed to the gradual increase in plate density and reduction in porosity at moderate pressures, which limits water ingress and thus lowers TS (Adhikari et al. 2018). However, when pressure exceeds a critical threshold, excessive compaction increases internal stress, potentially causing expansion upon water absorption and consequently increasing TS (Ge and Lu et al. 2024). As illustrated in Fig. 5, physical and mechanical properties exhibited minimal variation across different hot-pressing pressures (with insignificant maximum/minimum differences). This indicated that pressure had a limited influence on overall performance—consistent with the range and variance analysis results from Fig. 3 and Table 5. At 4 MPa, MOR did not meet industry standards; when pressure exceeds 4 MPa, MOE also falls below acceptable levels. Based on comprehensive evaluation, an optimal hot-pressing pressure for walnut shell-based wood particleboard is approximately 4 MPa, where the lowest 2hTS value is achieved.

Effect of Hot-pressing Duration on the Mechanical and Physical Properties of Walnut Shell-Based Wood Particleboard

Hot-pressing duration refers to the holding time in the hot-pressing process. The length of the hot-pressing duration strongly influences the mechanical properties of the plate, which will directly affect the curing, durability, and surface quality of the adhesive (Jiang et al. 2025). Therefore, selecting an appropriate hot-pressing duration is critical. The optimum hot-pressing duration for pressing walnut shell particleboard was explored. Under conditions of a hot-pressing pressure of 5 MPa, a hot-pressing temperature of 160 °C, and an adhesive application level of 14%, the effects of different hot-pressing durations on particleboard properties are shown in Fig. 6.